How to heat treat aluminum alloy？

How to heat treat aluminum alloy?

In addition to some common characteristics of aluminum alloys, such as high strength-to-weight ratio and strong corrosion resistance, the performance of different alloys is quite different, and heat treatment is also a tool to adjust its performance.

Heat treatment refers to controlling the temperature of part or all of the alloy and the time at a certain temperature, thereby changing its microstructure and changing the properties of the alloy.

Heat Treatment of Steel – Heating the metal to very high temperatures.

But aluminum has a much lower melting point and a higher thermal conductivity, which can significantly affect how it heats up.

Can aluminum alloy be heat treated?

Some specific alloys can be heat treated, not all aluminum alloys can be heat treated;

সাধারণভাবে বলতে, heat treatment can improve the performance parameters of aluminum alloys, যেমন:

• 1. Reinforced alloy
• 2. Increased ductility
• 3. Increased hardness
• 4. Eliminate internal stress
• 5. Improve its corrosion resistance
• 6. পরিবাহিতা

Alloys that can be strengthened by heat treatment are called heat treatable alloys, যেমন:

• 2000 সিরিজ
• 4000 সিরিজ (some alloys)
• 6000 সিরিজ
• 7000 সিরিজ
• 8000 সিরিজ

The factor that determines whether the alloy can be heat treated is the chemical composition of the alloy. Some chemical elements show higher solubility in aluminum at high temperature, and the atoms can be redistributed in the alloy to make the distribution more uniform and improve the performance of the alloy.

However our most common heat treatable alloy is 6061 খাদ.

What are the heat treatment methods of aluminum alloy?

There are four commonly used heat treatment methods for aluminum alloys;

1. Annealing

Annealing is a process used to counteract some of the effects of cold working (without heating the aluminum). When a material is cold worked, it creates internal stresses that increase its strength and hardness. যাহোক, this comes at the expense of some ductility and formability, an effect called work hardening.

Work hardening is necessary to increase the strength of the product. যাহোক, if the product is subsequently subjected to further molding processing, the decrease in formability may lead to processing failure of the product.

Annealing also relieves internal stresses in cast aluminum parts to prevent future cracks. The process involves heating the alloy to a specific temperature, holding it for a certain amount of time, and then slowly cooling it back to room temperature.

2. Solution heat treatment

Solution heat treatment involves a heating process similar to annealing, but instead of gradually cooling to room temperature, the product is quenched. Quenching is usually done in water and essentially “freezes” the microstructure before the atoms redistribute.

After quenching, aluminum is capable of age hardening. Quenching also provides a window that allows you to proceed with further forming processes.

Solution heat treatment maximizes the concentration of hardening alloying elements in solid solution so that they do not precipitate out before aging occurs.

The ideal temperature to achieve this solubility is only a few degrees below the melting temperature of the alloy. Due to the very narrow temperature window, very precise furnaces must be used to achieve and maintain the required conditions.

3. Natural and Artificial Aging

When a product is solution heat treated, aging is a natural or artificial process. The aging process gradually increases the strength and hardness of the alloy to a higher level than the initial level.

Once the aging process begins, the microstructure of the alloy gradually fixes as solid solution elements begin to precipitate and lock into their final positions.

Natural aging means that most of the hardening occurs within 24 hours of being treated, and it may take four to five days for full effect to take place. যাহোক, some alloys cannot achieve maximum strength through natural aging because their solid solution components cannot be completely precipitated.

These alloys require further heating to achieve complete precipitation, a process called artificial aging, also known as precipitation hardening. The alloy is heated at a specific temperature and held for 6 প্রতি 24 ঘন্টার, then cooled to room temperature. The result is an alloy with increased strength and hardness but reduced ductility.

4. Homogenization

The main goal of the final heat treatment process (homogenization) is to redistribute the internal alloying elements in order to achieve uniformity in the chemical composition of the product. This is very important for castings, which solidify at different rates throughout their thickness, starting at the edge of the mold.

In this process, elements with lower melting points, such as pure aluminum, solidify first at the outer edges, while elements with higher melting points migrate and concentrate toward the center of the casting wall.

If nothing is done, some areas of the product may be too soft, while other areas may be too hard and brittle, making failure more likely. To homogenize the aluminum alloy, the part is heated to a temperature just below its melting point and then cooled slowly.

The difference between homogenization and annealing is that homogenization is done at a higher temperature. Annealing only recrystallizes through grain boundary migration, while homogenization also allows the migration of alloying elements to achieve uniformity of chemical composition throughout the product.

Heat treatment and tempering: are they related?

When searching for aluminum alloys, the temper condition is generally included, and some temper designations are marked according to the specific heat treatment mentioned earlier. That is, the designations “O”, “W” and “T” respectively disclose whether the alloy has been annealed, solution heat treated or aged.

O = annealed

W = solution heat treated

T = old age

Their meanings are different, but a specific tempering treatment usually requires a specific heat treatment process;
When you are ready to order or use an aluminum alloy, it is best to remember its tempering name and the effect of tempering on the properties of the alloy.

Summarize

When purchasing aluminum alloy, not only to determine the alloy type, the alloy type can determine the performance of the alloy is good, but different tempering states have a relatively large impact on performance;

Let me give you an example to illustrate a problem. When purchasing the tempered state of alloy A and B, it is found that the tempered state of alloy C and D can also meet all the physical and chemical performance requirements. can be improved to a greater extent.

The suitability of heat treatment for your product will depend on its end application and the manufacturing process you choose. Since heat treatment incurs additional tooling costs, you should carefully evaluate whether it is necessary in your situation.