Surface passivation process of 5052 অ্যালুমিনিয়াম খাদ

পরিচিতি 5052 aluminum alloy and passivation process

As a non-ferrous metal material with excellent comprehensive properties, aluminum alloy is widely used in aerospace, নির্মাণ, অটোমোবাইল, mechanical equipment and other industries.

5052 অ্যালুমিনিয়াম খাদ is light in weight and has good weldability, so it is often used in the preparation of aluminum alloy automotive fuel tanks, গ্যাস স্টোরেজ ট্যাংক, operating platforms and other parts in the automobile manufacturing industry. যাহোক, the standard electrode potential of aluminum alloy is low, and it is easy to cause micro-battery corrosion in a humid environment (especially in a chlorine-containing humid environment), which seriously affects the corrosion resistance of aluminum alloy materials, and has a negative impact on its service life and engineering applications. have a huge negative impact.

Surface electrochemical treatment and chemical treatment are common methods for aluminum alloy anticorrosion. তাদের মধ্যে, electrochemical surface treatment of aluminum alloy has the disadvantages of complex equipment and high cost, and chemical passivation treatment has been widely used in recent years because of its low cost and high efficiency. আবেদন.
জন্য 5052 অ্যালুমিনিয়াম খাদ, an automotive exterior engineering material, it is still of great significance to seek a simple, low-cost and environmentally friendly corrosion passivation method.
Hexavalent chromium passivation is the most effective and most widely used chemical passivation. যাহোক, hexavalent chromium is toxic and carcinogenic, and has been gradually banned by more and more countries. In order to replace hexavalent chromium, researchers have successively developed technologies such as rare earth metal salt passivation, molybdate passivation, silicate passivation, and trivalent chromium salt passivation, among which the film-forming mechanism of hexavalent chromium is the same and non-toxic The trivalent chromium salt passivation performance is excellent, and it is most likely to replace the hexavalent salt passivation.
Although previous studies on the passivation of trivalent chromium are more, but less applied to aluminum alloys, and the key exterior parts of aluminum alloy automobiles have higher requirements for corrosion resistance, and trivalent chromium is suitable for adding organic complexing agents color passivation scheme. For this reason, on the basis of the previous research, this work selects the chemical passivation method of chromium sulfate salt with research potential, uses the addition of activator to improve the film quality, optimizes the passivation process parameters, and finally successfully develops an application Based on the trivalent chromium passivation process of 5052 অ্যালুমিনিয়াম খাদ, the passivation film formed is continuous and uniform in silver white, রঙে ইউনিফর্ম, good in gloss, excellent in corrosion resistance, non-polluting to the environment, and has a good application prospect .

Chromium sulfate passivation

Performance testing of passivated surfaces

Exterior

Based on the appearance requirements of automotive exterior parts, visually observe the passivation film formation, such as appearance color changes, film continuity and uniformity, and comprehensively evaluate the appearance quality of the passivation film.

Neutral salt spray test

According to the company’s requirements for 240h salt spray corrosion resistance of automotive aluminum alloy appearance parts, the test is carried out according to the neutral salt spray test (NSS test) method in GB/T10125-2012. The concentration of NaCl solution in the reagent is 5% (ভর ভগ্নাংশ), and the pH value is 6.5-7.2. The pressure of the saturated pressure chamber is 70-170kPa, the salt mist settlement per 80cm2 area is 1-2mL/h, and the test piece is 20° to the vertical direction.

The temperature of the test chamber is kept at (35±2)°সে, and the spraying is continued for 10 দিন. At the end of the test, wash the surface of the finished product with water and a soft brush, dry it, take pictures with a digital camera, observe the corrosion of the test piece, and according to GB/T12335-1990 “The metal coating is anodic to the substrate after the coating corrosion test”. Specimen Rating”, by calculating the corrosion area to rate the degree of corrosion defects on the surface appearance of the specimen.

Copper sulfate drop test

The corrosion resistance of aluminum alloy passivation film was tested by copper sulfate drop test. The composition of copper sulfate corrosion solution is 41g/L copper sulfate, 35g/LNaCl, 13mL/LHCl. In the test, use a dropper to drop a drop of copper sulfate corrosion solution on the surface of the sample at room temperature, observe the color change of the droplet, এটাই, the color changes from sky blue to black, and record the time of color change. The spot test of each sample takes the average value of the data of 5 different areas. The length of time can reflect the pros and cons of the corrosion resistance of the passivation film.

Factors Affecting Passivation Effect

Effect of Chromium Sulfate Concentration on Passive Film

In the passivation test, chromium sulfate, as a film-forming substance, affects the surface corrosion resistance by affecting the composition and structure of the conversion film.

Good film-forming quality depends on the matching between chromium sulfate and surfactant. Due to the increase of chromium sulfate concentration and insufficient amount of surfactant K2ZrF6, the surface activity is weakened, so the bonding between film-forming molecules and the matrix is weakened, making passivation The film forming is not complete, and the film quality becomes poor, which in turn makes the film durable Corrosion decline.

Effect of Potassium Fluozirconate Concentration on Passive Film

K2ZrF6 is used as the surface active component in the passivation solution, and its concentration also has an important influence on the film quality. In the passivation test, the main function of potassium fluorozirconate is to reduce the surface tension of aluminum alloy, activate the surface of the alloy, promote the full reaction of chromium sulfate and the substrate to form a uniform and dense film, and improve its corrosion resistance.

Effect of passivation time on passivation film

The passivation time mainly affects the thickness of the conversion film, and as an industrial application, an appropriate passivation time can reduce costs and save resources.

Summary of passivation process for 5052 অ্যালুমিনিয়াম খাদ

• (1) Based on the 5052 aluminum alloy sample, the optimum conditions for chemical passivation of chromium sulfate are: chromium sulfate 1.0g/L, potassium fluozirconate 2.5g/L, passivation time 3min, the passivation prepared under this condition The surface of the film has high gloss, uniform color and high corrosion resistance, meeting the requirements of 240h salt spray.
• (2) In the chromium sulfate passivation test, chromium sulfate, as a film-forming substance, mainly affects the composition and structure of the conversion film and makes the aluminum alloy surface in a passivation state. Its concentration must match the concentration of the activator potassium fluozirconate. If the chromium concentration is too high, the corrosion resistance of the passivation film will be affected. The main function of potassium fluorozirconate is to reduce the surface tension of aluminum alloy, activate the surface of the alloy, and promote the full reaction of chromium sulfate and the matrix. The concentration of potassium fluorozirconate is too low to play its role.
• (3) The passivation time mainly affects the film thickness of the passivation film and the degree of passivation reaction. If the time is too short, the reaction will not be sufficient, and the film-forming quality will be poor; if the time is too long, the film will be too thick, which will affect the appearance quality such as surface color and waste resources.