Aluminum Alloy Density Data Sheet

Some questions about the density of aluminum alloy?

What is the density of industrial aluminum?

Jak všichni víme, aluminum is a light material. We usually record the density of aluminum as 2700kg/m3; there are many units to express the density of aluminum, such as kg/m3, g/cm3, lbs/m3, lbs/cm3, lb/in3

Conversion Between Density Units

2700kg/m3 converted to g/cm3:

2700kg = 2700000g

1m3 = 100x100x100cm3 = 1000000cm3

2700kg/m3 = 2700000g/1000000cm3 = 2.7g/cm3

2700kg/m3 is converted to lb/m3, lb/cm3:

Putting 1 (Kilogramy) = 2.20462262 (Libra, lb) into the formula gives:

2700kg = 5952.481078995lbs

2700kg/m3 = 5952.481078995 lbs/m3 = 5952.481078995 lbs/1000000cm3 = 0.00595 lbs/cm3

2700kg/m3 converted to lb/in3:

Put 1cm = 0.39370 inch into the formula to get

0.00595 lbs/cm3 = 0.00595 lbs/0.39370 inches x 0.39370 palce x 0.39370 inches = 0.00595 lbs/0.061 in3 = 0.0975 lbs/in3

Through unit conversion, the expressions of pure aluminum density are 2700kg/m3, 2.7g/cm3, 5952.481078995 lbs/m3, 0.00595 lbs/cm3, 0.0975 lbs/in3, atd.;

Why different grades of alloy aluminum have different densities?

In addition to pure aluminum, any alloy type of aluminum alloy has added different elements in its production process, such as Si, Fe, Cu, Mn, Mg, Cr, Zn, Z, atd. The density of these elements is different from that of aluminum , so the density of the produced aluminum alloy will also be different from that of pure aluminum;
Například, the main additive element of 3 series aluminum alloy is Mn, so it is usually called Al-Mn alloy, the main additive elements of 5 series aluminum alloy are Mn and Mg, also called Al-Mn-Mg alloy, jejich hustota je podobná jako u čistého hliníku bude jiná;

Živel	Al	A	Fe	Cu	Mn	Mg	Cr	Zn	Z
Hustota	2.7	2.33	7.874	8.96	7.21	1.738	7.19	7.14	4.506

Different Alloy Aluminum Density Table

Density of Aluminum & Slitina hliníku

Hliník a hliníková slitina	Hustota (g/cm3)	Hustota (kg/m3)	Hustota (lbs/in3)	Hustota (lbs/ft3)
1050	2.71	2705	0.0977	168.87
1060	2.71	2705	0.0977	168.87
1100	2.71	2710	0.0979	169.18
1145	2.70	2700	0.0975	168.56
1175	2.70	2700	0.0975	168.56
1200	2.70	2700	0.0975	168.56
1230	2.70	2700	0.0975	168.56
1235	2.71	2705	0.0977	168.87
1345	2.71	2705	0.0977	168.87
1350	2.71	2705	0.0977	168.87
2011	2.83	2830	0.1022	176.67
2014	2.80	2800	0.1012	174.80
2017	2.79	2790	0.1008	174.17
2018	2.82	2820	0.1019	176.05
2024	2.78	2780	0.1004	173.55
2025	2.81	2810	0.1015	175.42
2036	2.75	2750	0.0994	171.68
2117	2.75	2750	0.0994	171.68
2124	2.78	2780	0.1004	173.55
2218	2.81	2810	0.1015	175.42
2219	2.84	2840	0.1026	177.30
2618	2.76	2760	0.0997	172.30
3003	2.73	2730	0.0986	170.43
3004	2.72	2720	0.0983	169.80
3005	2.73	2730	0.0986	170.43
3105	2.72	2720	0.0983	169.80
4032	2.68	2680	0.0968	167.31
4043	2.69	2690	0.0972	167.93
4045	2.67	2670	0.0965	166.68
4047	2.66	2660	0.0961	166.06
4145	2.74	2740	0.0990	171.05
4343	2.68	2680	0.0968	167.31
4643	2.69	2690	0.0972	167.93
5005	2.70	2700	0.0975	168.56
5050	2.69	2690	0.0972	167.93
5052	2.68	2680	0.0968	167.31
5056	2.64	2640	0.0954	164.81
5083	2.66	2660	0.0961	166.06
5086	2.66	2660	0.0961	166.06
5154	2.66	2660	0.0961	166.06
5183	2.66	2660	0.0961	166.06
5252	2.66	2660	0.0961	166.06
5254	2.66	2660	0.0961	166.06
5356	2.64	2640	0.0954	164.81
5454	2.69	2690	0.0972	167.93
5456	2.66	2660	0.0961	166.06
5457	2.69	2690	0.0972	167.93
5554	2.69	2690	0.0972	167.93
5556	2.66	2660	0.0961	166.06
5652	2.67	2670	0.0965	166.68
5654	2.66	2660	0.0961	166.06
5657	2.69	2690	0.0972	167.93
6003	2.70	2700	0.0975	168.56
6005, 6005A	2.70	2700	0.0975	168.56
6053	2.69	2690	0.0972	167.93
6061	2.70	2700	0.0975	168.56
6063	2.70	2700	0.0975	168.56
6066	2.72	2720	0.0983	169.80
6070	2.71	2710	0.0979	169.18
6101	2.70	2700	0.0975	168.56
6105	2.69	2690	0.0972	167.93
6151	2.71	2710	0.0979	169.18
6162	2.70	2700	0.0975	168.56
6201	2.69	2690	0.0972	167.93
6262	2.72	2720	0.0983	169.80
6351	2.71	2710	0.0979	169.18
6463	2.69	2690	0.0972	167.93
6951	2.70	2700	0.0975	168.56
7005	2.78	2780	0.1004	173.55
7008	2.78	2780	0.1004	173.55
7049	2.84	2840	0.1026	177.30
7050	2.83	2830	0.1022	176.67
7072	2.72	2720	0.0983	169.80
7075	2.81	2810	0.1015	175.42
7175	2.80	2800	0.1012	174.80
7178	2.83	2830	0.1022	176.67
7475	2.81	2810	0.1015	175.42
8017	2.71	2710	0.0979	169.18
8030	2.71	2710	0.0979	169.18
8176	2.71	2710	0.0979	169.18
8177	2.70	2700	0.0975	168.56

Density analysis of different aluminum alloys

Podle analýzy ve výše uvedené tabulce, slitiny s nejnižší hustotou jsou 5056 a 5356, a jejich hustota je 2.63, která je nižší než 2.7 z čistého hliníku;

Chemical composition table of 5056 slitina hliníku

Živel	AL	Mg	Mn	Cr
Obsah (%)	95.0	5.0	0.12	0.12
Hustota prvků	2.7	1.738	7.21	7.19

Vzhledem k chemickému složení 5056 je mg kromě al, hustota mg je 1.738, která je nižší než 2.7 z al, takže můžeme zhruba soudit, že hustota 5056 hliníková slitina je nižší než u čistého hliníku, což je 2,7 g/cm3;

The densest aluminum alloy grade

Typy slitin s nejvyšší hustotou jsou 2219 a 7049, a jejich hustota je 2.84, který je 0.14 vyšší než u čistého hliníku;

Chemical composition table of 2219 slitina hliníku

Živel	Al	Cu	Mn	Zr	PROTI	Z
Obsah (%)	93	6.3	0.3	0.18	0.10	0.06
Hustota prvků	2.7	8.93	7.21	6.49	6.11	4.506

Z tabulky složení slitiny, lze usoudit, že nejvíce přidaný prvek v 2219 je s, a hustota cu je 8.93, což je trojnásobek hustoty hliníku, což výrazně zvyšuje hustotu 2219 slitina hliníku; a další prvky obsažené v 2219 slitina hliníku Hustota prvku je také větší než 2,7 g/cm3, takže hustota 2219 slitin hliníku je mnohem vyšší než u čistého hliníku;