3004 alloy foil is a common product in the aluminum-magnesium-manganese alloy series. 왜냐하면 3004 aluminum foil contains manganese and magnesium alloy elements, it has excellent anti-rust properties and is also called anti-rust aluminum alloy. 참조: 위키피디아;
3004 알루미늄 호일
| AL3004 aluminum foil metal composition (%) | |||||||||
| 합금 | 시 | 철 | 구 | 미네소타 | 마그네슘 | 증권 시세 표시기 | 의 | 다른 | 알 |
| 3004 | 0.3 | 0.7 | 0.25 | 1.5 | 0.8-1.3 | 0.25 | 0.1 | 0.2 | ≥90 |
의 힘 3004 aluminum alloy foil is 10% higher than that of series 1 알루미늄 호일, 그리고 그것은 좋은 성형 성을 가지고 있습니다, 용접성 및 내식성. For processing, 3004 aluminum foil has good formability and high corrosion resistance, and can meet the environment required for processing.
| 합금 성질 | 인장 강도 | 항복 강도 | 신장(mm) | ||
| 3004-영형 | 115-175MPa | 16,700-25,400 psi | 70-140 MPa | 10,000-20,300 psi | 25% |
| 3004-H14 | 140-185 MPa | 20,300-26,800 psi | 25-165 MPa | 18,100-24,000 psi | 6-10% |
| 3004-H16 | 165-205 MPa | 23,900-29,700 psi | 150-190 MPa | 21,800-27,600 psi | 4-8% |
| 3004-H18 | 185-225 MPa | 26,800-32,600 psi | 175-210 MPa | 25,400-30,500 psi | 3-7% |
| 3004-H22 | 140-185 MPa | 20,300-26,800 psi | 125-165 MPa | 18,100-24,000 psi | 6-10% |
| 3004-H24 | 165-205 MPa | 23,900-29,700 psi | 150-190 MPa | 21,800-27,600 psi | 4-8% |
| 3004-H26 | 185-225 MPa | 26,800-32,600 psi | 175-210 MPa | 25,400-30,500 psi | 3-7% |
| 3004-H28 | 215-255 MPa | 31,200-37,000 psi | 205-240 MPa | 29,700-34,800 psi | 2-6% |
3004 aluminum foil is widely used in food packaging, 컨테이너 호일, and aluminum foil lunch boxes.
●Aluminum foil containers:
Aluminum foil containers made of Huawei 3004 aluminum foil are stronger than 3003 알루미늄 호일. 3004 aluminum foil has both the price advantage of 8011 알루미늄 호일 and the strength advantage of 3003 알루미늄 호일.
3004 aluminum foil containers have neat appearance and good thermal conductivity. It can be heated directly in the original packaging using oven, microwave, steamer and other kitchen utensils.
●Honeycomb aluminum foil:
The aluminum honeycomb core is a hexagonal aluminum honeycomb structure, which is widely used in decorative materials, 가전 제품, 조명 산업, 운송 산업, and furniture industry. The raw material of the aluminum honeycomb core is 3004 알루미늄 호일, H18/H19 status, 고강도, 가공 후 변형되기 쉽지 않음, the surface of the aluminum foil is degreased and clean, and the glue is not easy to fall off.
The strength is much higher than that of 1100 알루미늄 호일. The processed product is not easy to deform, the end face is flat, the edges are burr-free, and the layout after adhesive lamination is highly flat.
●Air conditioning foil:
Common air conditioning aluminum foils include 1100/3003/3004/8011 합금, 등. 그만큼 3004 aluminum foil used as fin material for air conditioning heat exchangers is an aluminum-manganese alloy with good corrosion resistance, 우수한 성형성, high strength and elongation, 등., and meets the mechanical performance requirements of air conditioning foils.
At room temperature (25°C or 77°F), the density of 3004 aluminium foil is approximately 2.71g/cm³(2.7×10³kg/m³). This value is a typical density for aluminum alloys (포함 3004) and may vary slightly depending on the specific manufacturing process and the exact composition of the foil.
The melting point of aluminum alloy 3004 is approximately 658-660°C (1216-1220°F). This is the temperature at which the solid aluminum in the foil transforms into a liquid state.
알루미늄 합금 3004 foil has a variety of performance characteristics to suit a variety of applications.
1.3004 foil has good formability and can be easily formed into different structures without cracking or breaking.
2. 내식성: 3004 alloy has good corrosion resistance and is suitable for use in environments with moisture and other corrosive factors.
3. 강도와 내구성: 3004 provides sufficient strength for the intended application.
4. High-quality printing: 3004 aluminum foil has a smooth and consistent surface, making it ideal for high-quality printing and branding, 식품 포장과 같은.
5. 내열성: It has good heat resistance, which makes it suitable for applications that involve heat exposure or need to act as a thermal barrier.
6. 경량: 3004 알루미늄 호일은 가벼운 소재입니다..
7. 연성: 3004 aluminum foil is ductile and can be easily stretched and bent without breaking.
중국 시장의 주요 알루미늄 서클 제조업체 중 하나, 우리의 알루미늄 원형은 제일 원료 및 기계로 만듭니다, 주요 제품은 다음을 포함합니다 1000 시리즈, 3000 시리즈, 5000 시리즈와 8000 시리즈, 이상의 출력으로 5000 톤/월
다이아몬드 알루미늄 시트는 한쪽 면에 융기된 다이아몬드 패턴이 있는 알루미늄 시트 유형입니다., 젖고 미끄러운 조건에서 우수한 미끄럼 방지 및 견인력을 제공합니다..
5454 알루미늄 시트는 강력한 녹슬지 않는 능력을 가지고 있으며 5000 시리즈 알루미늄-마그네슘 합금. 5454 알루미늄 시트는 또한 비열처리 합금이며 20% 보다 강함 5052 알루미늄 시트. 해양 시설 파이프라인에 자주 사용됩니다., 알루미늄 탱크 차체 및 기타 분야.
허난 화웨이 알루미늄 유한 회사, 주식 회사, 중국 허난에서 가장 큰 알루미늄 공급 업체 중 하나,우리는 2001년에 설립되었으며 수입 및 수출 및 고품질 알루미늄 제품에 대한 풍부한 경험을 가지고 있습니다.
월~토, 8오전 – 오후 5시
일요일: 닫은
© 저작권 © 2023 허난화웨이알루미늄, 주식 회사
최신 댓글
귀하에게, Please offer your best FOB Prices specs are as under ALUMINIUM STRIP (AL=99.50% 최소) 크기:450 X32 X6 MM. 당신의 하나 570 EN-AW 1050 ㅏ, 수량=3400KG
안녕하세요, 다음과 같이 항목을 제공하는 것이 친절하겠습니까?: 코일 0,6х1250 (1000)mm EN AW-3105 5tons
안녕하세요, 알루미늄 판을 제공 할 수 있습니까?? 사실 나는 필요하다.: 110mm x 1700mm x 1700mm 5083 H111 - 21 pcs Next year planed is 177 PCS (개)
훌륭한 기사. 나는 기뻤다, 나는이 기사를 발견. 많은 사람들이, 그들이 그것에 대해 정확한 지식을 가지고 있다는 것, 하지만 종종 그렇지 않다. 따라서 나의 즐거운 놀라움. 나는 감동. 나는 확실히이 장소를 추천하고 더 자주 돌아올 것입니다, 새로운 것을 보기 위해.
알루미늄 스트립의 요구 사항