Knowledge about tempering of aluminum plate

Knowledge about tempering of aluminum plate

Tempering is a heat treatment process that is used to improve the mechanical properties of aluminum alloys, 強さも含めて, 硬度, and toughness.
The tempering process involves heating the material to a specific temperature and then cooling it at a controlled rate.

3003 h14 aluminum sheet

What does the “O” stand for during tempering

The letter “O” in aluminum temper designations stands for “annealed,” which indicates that the aluminum has been softened through the annealing process.
Annealing involves heating the material to a specific temperature and holding it at that temperature for a period of time to allow for uniform heating. This process relieves any internal stresses or strains in the material and makes it more ductile and workable.

Other common temper designations for aluminum

Aluminum temper designations consist of a letter followed by one or more numbers. The letter indicates the tempering process, while the numbers indicate the specific details of the process. In addition to “O” (焼きなましされた), other common temper designations for aluminum include:

F: Without heat treatment, the state before heating is called F;
H: The “H” temper designation for aluminum refers to a group of alloys that have been strain-hardened, also known as cold-worked.
Strain hardening is a process where the aluminum is worked or deformed at room temperature, such as by rolling, 曲げ, or stretching. This causes the aluminum to become stronger and harder, but also less ductile.

The “H” temper designation is followed by one or more numbers that indicate the specific degree of strain hardening. The higher the number, the greater the amount of strain hardening and the higher the strength and hardness of the aluminum.
例えば, 3003 H14 has a lower degree of strain hardening than 3003 H32, which in turn has a lower degree of strain hardening than H36.

knowledge about tempering of aluminum plate

T: T is a mood designation that indicates thermally treated aluminum. しかし, there are numerous treatments which could full underneath the T designation. As an instance, T1 signifies aluminum that is nicely cooled down from an extended temperature shaping method, then clearly aged to a substantially solid situation. 一方で, T5 represents aluminum this is cooled from increased temperature shaping tactics and artificially elderly.
The temper designation is important in determining the mechanical properties of the aluminum, その強さも含めて, 硬度, and ductility, and can be used to ensure that the material is suitable for a particular application.