This standard applies to the dimensional tolerances of wrought aluminum and aluminum alloy rolled plates and strips.
Rolled products with a rectangular cross-section, uniform thickness and greater than 0.20mm, usually cut or sawn at the edges, and delivered in a straight shape. The thickness does not exceed 1/10 of the width.
A rolled product with a rectangular cross-section and a uniform thickness greater than 0.20 んん. Usually the edges are slit and delivered in rolls. The thickness does not exceed 1/10 of the width.
Finished products with a width greater than 1500mm or a length greater than 4000mm are called large-size plates.
5A03, 5A05, 5A06, 5083, 5086, 5A41 and other aluminum-magnesium alloy ordinary grade plates and strips with an average magnesium content greater than or equal to 3% and a thickness greater than or equal to 4.0mm, the allowable deviation is ±5% of the nominal thickness, The allowable deviation of the thickness of other aluminum and aluminum alloy ordinary grade plates and strips shall comply with the provisions in the table below.
| 厚さ | The specified width | |||||||
| ≤1000 | ＞1000～1500 | ＞1500～2000 | ＞2000～2500 | |||||
| 厚さの許容差 | ||||||||
| シート | Strip | シート | Strip | シート | Strip | シート | Strip | |
| ＞0.20～0.40 | ±0.05 | ±0.05 | ±0.06 | ±0.06 | — | — | — | — |
| ＞0.40～0.63 | – 0.10 | ±0.05 | – 0.14 | ±0.08 | – 0.18 | ±0.09 | – 0.24 | ±0.12 |
| ＞0.63～0.80 | – 0.12 | ±0.06 | – 0.14 | ±0.08 | – 0.18 | ±0.10 | – 0.26 | ±0.13 |
| ＞0.80～1.00 | – 0.15 | ±0.08 | – 0.17 | ±0.09 | – 0.20 | ±0.11 | – 0.29 | ±0.15 |
| ＞1.00～1.20 | – 0.15 | ±0.08 | – 0.17 | ±0.10 | – 0.22 | ±0.12 | – 0.29 | ±0.15 |
| ＞1.20～1.60 | – 0.20 | ±0.10 | – 0.25 | ±0.13 | – 0.27 | ±0.14 | – 0.29 | ±0.15 |
| ＞1.60～2.00 | – 0.20 | ±0.10 | – 0.26 | ±0.13 | – 0.28 | ±0.15 | – 0.30 | ±0.18 |
| ＞2.00～2.50 | – 0.25 | ±0.13 | – 0.29 | ±0.15 | – 0.30 | ±0.16 | – 0.32 | ±0.18 |
| ＞2.50～3.20 | – 0.30 | ±0.15 | – 0.34 | ±0.17 | – 0.35 | ±0.18 | – 0.36 | ±0.23 |
| ＞3.20～4.00 | – 0.30 | ±0.15 | – 0.36 | ±0.20 | – 0.37 | ±0.23 | – 0.38 | ±0.25 |
| ＞4.00～5.00 |
+ 0.10 – 0.35 |
±0.23 |
+ 0.10 – 0.37 |
±0.25 |
+ 0.10 – 0.42 |
±0.28 |
+ 0.10 – 0.45 |
±0.30 |
| ＞5.00～6.30 |
+ 0.10 – 0.40 |
±0.25 |
+ 0.10 – 0.42 |
±0.28 |
+ 0.10 – 0.42 |
±0.33 |
+ 0.10 – 0.45 |
±0.38 |
| ＞6.30～8.00 |
+ 0.10 – 0.45 |
±0.30 |
+ 0.10 – 0.47 |
±0.36 |
+ 0.10 – 0.50 |
±0.38 |
+ 0.10 – 0.60 |
±0.46 |
| ＞8.00～10.00 |
+ 0.10 – 0.50 |
±0.38 |
+ 0.10 – 0.50 |
±0.43 |
+ 0.10 – 0.50 |
±0.51 |
+ 0.10 – 0.60 |
±0.58 |
| ＞10.00～16.00 | ±0.50 | ±0.50 | ±1.0 | ±1.5 | ||||
| ＞16.00～25.00 | ±0.75 | ±0.75 | ±1.5 | ±2.0 | ||||
| ＞25.00～40.0 | ±1.0 | ±1.0 | ±1.5 | ±2.0 | ||||
| ＞40.00～60.00 | ±1.5 | ±1.5 | ±2.0 | ±3.0 | ||||
| ＞60.00～80.00 | ±3.0 | ±3.0 | ±3.5 | ±4.0 | ||||
| ＞80.00～100.00 | ±3.5 | ±3.5 | ±5.0 | ±5.5 | ||||
| ＞100.00～160.00 | — | ±4.0 | ±5.5 | ±6.0 | ||||
| 注記: For plates with asymmetrical deviation, when symmetrical deviation is required, the deviation of the corresponding strip can be adopted through negotiation between the two parties. | ||||||||
4.1 For common-grade plates with a thickness greater than 40mm, after rolling with the whole ingot, the head and tail are not cut, and the whole block is delivered.
4.2 The nominal length of the variable-section plate is calculated by the nominal thickness and average wedge degree of the thin end and thick end.
4.3 The length deviation of ordinary grade plates shall meet the requirements in the table below.
| Nominal thickness | Length Allowable Deviation | Nominal thickness | Length Allowable Deviation |
| ≤4.50 |
+25 – 5 |
＞10.0～40.0 | ±40 |
| ＞4.50～10.00 | ±25 | Variable break panel ≤5.0 (thick end) |
+50 0 |
The permissible deviation of the width of common-grade boards is in accordance with the regulations in the table below.
| 厚さ | 幅 | Allowable deviation | |
| ≤4.5 | ≤1000 |
+5 -3 |
|
| ＞1000～2000 |
+10 – 5 |
||
| ＞2000～2400 | ±10 | ||
| ＞4.5 | Cut edge |
+30 -10 |
|
| No trimming | 5A03, 5A05, 5A06, 5083 and other aluminum-magnesium alloys with an average magnesium content greater than or equal to 3% and 7A09, 7A04, 7075 |
+150 0 |
|
| Other alloys and pure aluminum |
+120 0 |
||
| 注記: For plates with a thickness ≤4.5mm that have been heat-treated in a salt bath furnace, and for large-size plates with a length >4000んん, the allowable width deviation is | |||
3003 h14 アルミニウム コイルは、h14 焼き戻しを指します。 3003 アルミニウムコイル。そしてH14焼き戻しは通常、取得することを意味します 1/2 硬さによる強さ.
中国市場における主要なアルミサークルメーカーの一つとして, 当社のアルミニウムサークルは最高の原材料と機械で作られています, 主な製品には以下が含まれます 1000 シリーズ, 3000 シリーズ, 5000 シリーズと 8000 シリーズ, 以上の出力で 5000 トン/月
利用可能なさまざまなアルミニウム合金の中から, の 2014 アルミニウム板はそれ自体でニッチを切り開いた, 特に高い強度が要求される用途において, 優れた機械加工性, そして疲労に対する抵抗力.
5754 アルミ板は加工性に優れているのが特徴です, 良好な耐食性, 溶接性と成形の容易さ. 鍛造合金として, 5754 アルミニウムシートは圧延によって形成できます, 押し出し, そして鍛造, ただしキャストではありません.
アルミニウム合金 8011 アルミ箔は、アルミプラスチック複合板のベーステープや食品包装に広く使用されています。. プロのアルミホイルとして 8011 中国のメーカー, ファーウェイのアルミニウムは、 8011 アルミ箔の生産拠点として、 20 長年にわたる豊富なアルミ箔生産経験と熟練した加工技術.
河南華為アルミニウム有限公司, 株式会社, 中国河南省最大のアルミニウムサプライヤーのひとつ,私たちは2001年に設立され、輸出入と高品質のアルミニウム製品の豊富な経験があります
月～土, 8午前 – 午後 5 時
日曜日: 閉まっている
© 著作権© 2023 河南華為アルミニウム有限公司, 株式会社
最新のコメント
拝啓, Please offer your best FOB Prices specs are as under ALUMINIUM STRIP (AL=99.50% 最小) サイズ:450 X32 X6MM. あなたのもの 570 EN-AW 1050 あ, 数量=3400KG
こんにちは, 以下の商品を提供していただけませんか: コイル 0,6х1250 (1000)mm EN AW-3105 5tons
こんにちは, アルミ板を提供してもらえますか? 実際には必要です: 110mm×1700mm×1700mm 5083 H111 - 21 pcs Next year planed is 177 個
素晴らしい記事. 私は喜んでいました, この記事を見つけたこと. 多くの人がそう思っています, 彼らはこの件に関して信頼できる知識を持っていること, しかし、そうでないこともよくあります. したがって、私の嬉しい驚きは. 私が感銘を受けた. この場所を絶対にお勧めし、もっと頻繁に戻ってきます, 新しいものを見るために.
アルミニウムストリップの要件