とは 3105 アルミコイル?

です 3000 シリーズアルミニウム合金: 主な合金添加物はマンガンです, 鍛造品の一次成形用に配合されています。. It has good rust resistance, 優れた溶接性, and good electrical conductivity. The conductivity can reach 41%.

Price of 3105 アルミコイル

This aluminum metal has excellent formability and weldability, but does not respond to heat treatment. 3000 series aluminum metal is 20% より強い 1000 series metal.

よりも強いです 1000 シリーズ合金, but its price is almost the same as 1000 シリーズ合金, so it is widely used in making roofing.

In the European standard, we name it EN AW-3105. また, the UNS number is A93105.

から:

Specifications of Alloy Aluminum Coil 3105

テンパーズ:
3105-O Aluminum，3105-H111 Aluminum，3105-H12 Aluminum，3105-H14 Aluminum，3105-H16 Aluminum，3105-H18 Aluminum，3105-H19 Aluminum，3105-H22 Aluminum，3105-H24 Aluminum，3105-H25 Aluminum，3105-H26 Aluminum，3105-H28 Aluminum

Aluminum slitting capabilities
Gauge Range	.004″ to .190″ (.102 mmから 4.826 んん)
Width Range	.250″ to 60″ (6.365 mmから 1524 んん)
ID	8, 12, 16 または 20 (インチ)
OD	78″ maximum
Coil Weight	40,000 lbs maximum
Cut-to-length capabilities
Gauge Range	.015 に .060 (.381 mmから 1.524 んん)
Width Range	8” – 48” (203 mmから 1.219 んん)
Length Range	12” to 144” (305 mmから 3.658 んん)

アルミコイル 3105 化学組成
要素	パーセンテージ (%)
アルミニウム (アル)	残り
ケイ素 (そして)	0.6 最大
鉄 (鉄)	0.7 最大
銅 (銅)	0.3 最大
マンガン (ん)	0.3~0.8
マグネシウム (マグネシウム)	0.2~0.8
クロム (Cr)	0.2 最大
亜鉛 (亜鉛)	0.4 最大
チタン (の)	0.1 最大
Remainder Each	0.05 最大
Remainder Total	0.15 最大

の性質 3105 – H12 temper (¼ hard) アルミコイル
厚さ (インチ)	Yield Strength Min. (クシ)	抗張力 (クシ)		伸長 (%) 分.
厚さ (インチ)	Yield Strength Min. (クシ)	分.	マックス.
0.017 – 0.019	15.0	19.0	26.0	1
0.020 – 0.031	15.0	19.0	26.0	1
0.032 – 0.050	15.0	19.0	26.0	2
0.051 – 0.080	15.0	19.0	26.0	3

の性質 3105 – H14 temper (½ hard) アルミコイル
厚さ (インチ)	Yield Strength Min. (クシ)	抗張力 (クシ)		伸長 (%) 分.
厚さ (インチ)	Yield Strength Min. (クシ)	分.	マックス.
0.017 – 0.019	18.0	22.0	29.0	1
0.020 – 0.031	18.0	22.0	29.0	1
0.032 – 0.050	18.0	22.0	29.0	2
0.051 – 0.080	18.0	22.0	29.0	2

3105 Alloy Aluminum Coil Features

Has excellent resistance to correction, 成形性, and welding characteristics.
Has average machinability. しかし, the machinability is improved in the harder tempered condition compared to the annealed condition.
Except for annealing during cold working, there is no reaction to heat treatment. Cold work properties are very good, even in the harder cold work condition.

Is 3105 Aluminum Bendable?

For annealed H12, H14, and H16 tempers, a bend radius in the thickness range of 1 に 2 t is recommended. H18 tempering should use a bend radius of 2 に 7 t.

違いは何ですか 3105 H24 And 3003H14?

The differences between 303H14 and 3105 H24 are as follows:

One of these is Brinell hardness; 3003 H14は 42 BHNと 3105 H24 には 47 BHN.

Another difference is fatigue strength; 3003 H14 is only 60 MPa, その間 3105 H24 is 74 MPa.

3105 H24 vs 3003H14 aluminum alloy

合金組成では, 3003 H14 contains more magnesium than 3105 H24. しかし 3105 H24 contains a small amount of titanium, chromium and copper that 3003 H14にはありません.

の適用 3105 Alloy Metal Aluminum Coil

アルミニウム 3105 is most commonly used where paint is required;
Typical applications include more general sheet metal work required;
Higher strength than 1000 シリーズアルミニウム合金, 住宅用サイディング;
Room dividers, baffles, トレーラーハウス, 雨具, and sign making.